软木
C - 12
L |
50 + 100 m |
D |
1.6 mm |
B |
50, 100 mm |
HB |
100 °C |
PDF Download
C - 12 / S
L |
50 + 100 m |
D |
1.6 mm |
B |
50, 100 mm |
HB |
100 °C |
PDF Download
C - 12 / 3.2
L |
100 m |
D |
3.2 mm |
B |
50 mm |
HB |
100 °C |
PDF Download
C - 12/S/SK/0.8
L |
30 + 150 m |
D |
0.8 mm |
B |
50, 100 mm |
HB |
100 °C |
PDF Download
C - 12 / SE
L |
50 + 100 m |
D |
1.6 mm |
B |
50, 100 mm |
HB |
90 °C |
PDF Download
尺寸
Article | Length in m | Width in mm | Weight in g/m² | Thickness in mm |
C - 12 |
50 + 100 ( -3 / +5 ) |
50, 100 |
1.300 |
1,6 (+/- 0,25) |
C - 12 / S |
50 + 100 ( -3 / +5 ) |
50, 100 |
1.200 |
1,6 (+/- 0,25) |
C - 12 / 3.2 |
— 100 ( -3 / +5 ) |
50 |
2.160 |
3,2 (+/- 0,25) |
C - 12/S/SK/0.8 |
30 + 150 ( -3 / +5 ) |
50, 100 |
1.350 |
0,8 (+/- 0,25) |
C - 12 / SE |
50 + 100 ( -3 / +5 ) |
50, 100 |
1.500 |
1,6 (+/- 0,25) |
涂层
Article |
Kind of Coating |
Hardness of Coating in ° |
Colour |
Abrasion |
C - 12 |
SBR / NBR filled with cork |
|
beige |
< 35 mg / 100 cm² |
C - 12 / S |
SBR - filled with granulated cork |
42 Shore A |
black |
< 130 mg / 100 cm² |
C - 12 / 3.2 |
SBR/NBR-filled with cork |
35-50 Shore A |
beige |
< 35 mg / 100 cm² |
C - 12/S/SK/0.8 |
SBR - filled with granulated cork |
42 Shore A (+/- 5) |
black |
< 130 mg / 100 cm² |
C - 12 / SE |
TPO - filled with granulated cork |
58 Shore A (+/- 3) |
black |
< 80 mg / 100 cm² |
载体信息
Article | Fabric | Tensile strength in N/cm | Adhesion strength in N/cm |
C - 12 |
Cotton / Polyester |
> 700 / 5 |
> 650 / 5 |
> 90 / 5 |
C - 12 / S |
CO |
> 450 / 5 |
> 450 / 5 |
> 90 / 5 |
C - 12 / 3.2 |
CO/Polyester |
> 700 / 5 |
> 650 / 5 |
> 90 / 5 |
C - 12/S/SK/0.8 |
CO |
> 450 / 5 |
> 450 / 5 |
> 90 / 5 |
C - 12 / SE |
CO |
> 450 / 5 |
> 450 / 5 |
> 70 / 5 |
抵抗力
Article |
Heat in °C |
Acids |
Liquids |
Oil |
Greave |
Hot water |
|
 |
 |
 |
 |
 |
 |
C - 12 |
100 |
• |
• |
• |
• |
|
C - 12 / S |
100 |
• |
• |
• |
• |
|
C - 12 / 3.2 |
100 |
• |
• |
• |
• |
|
C - 12/S/SK/0.8 |
100 |
• |
• |
• |
• |
|
C - 12 / SE |
90 |
• |
• |
• |
• |
|